Laboratory Evaluation of the Effect of the Combination of Zinc Nano Oxide and Basalt Fiber on the Performance of Bitumen and Asphalt Mixture

Authors

Department of Civil Engineering, Malard Branch, Islamic Azad University, Malard, Tehran, Iran.

Abstract

In order to improve the quality of road performance and solve the problem of deterioration in normal asphalt pavement during service, in this research, a 5.3% aluminate agent was used to modify the surface of nano zinc oxide and prepare composite modified asphalt with nano oxide and basalt fiber 1 (BF). It was used as a modifier. First, the initial performance of the different types was examined. Then, a dynamic shear rheology test was conducted to analyze the high temperature rutting performance of composite modified asphalt at different temperatures and frequencies. Then, using the flexural creep hardness test, the low temperature properties of asphalt modified with composite were investigated. The results show that the aging performance of asphalt modified with ZnO/BF nanocomposite is significantly improved after adding fibers to the modified asphalt. The average mass loss ratio is only 0.192%. At 46°C, the rutting coefficient of composite-modified asphalt increased by 62.3%. The main frequency curve is always at the highest position and continues to increase, indicating a significant improvement in the high-temperature rutting performance of the composite-modified asphalt. At 24°C, the S value of the creep modulus of asphalt modified with composite increased by 24.9%. In addition, there is no obvious effect of low temperature improvement, but the range of variation of creep tangent slope m of modified asphalt is reduced after aging, which further indicates that the addition of a modifier can reduce the effect of aging on asphalt.

Keywords

References

-Abdelsalam, M. Yue, Y. Khater, A. Luo, D. Musanyufu, J. Qin, X.  (2020). Laboratory Study on the Performance of Asphalt Mixes Modified with a Novel Composite of Diatomite Powder and Lignin Fiber. Appl. Sci. 10, 5517.
-Celauro, C. Praticò, F. (2018). Asphalt mixtures modified with basalt fibres for surface courses. Constr. Build. Mater. 170, 245–253.
-Dong, T.  (2020). Study on the Properties of Nano-ZnO/SBS/SBR Composite Modified Materials; Chongqing Jiaotong University: Chongqing, China.
-Fu, Z. Huang, Z. Ma, F. (2016). Effect of basalt fiber on road performance of aged asphalt mixture. Mater. Bull. 30, 118–122.
-Gu, Q. Kang, A. Li, B. Xiao, P. Ding, H. (2022). Effect of fiber characteristic parameters on the high and low temperature rheological properties of basalt fiber modified asphalt mortar. Case Stud. Constr. Mater. 17, e01247.
-Mansour, F. Ehsan, S. (2021). The effects of nano zinc oxide (ZnO) and nano reduced graphene oxide (RGO) on moisture susceptibility property of stone mastic asphalt (SMA). Case Stud. Constr. Mater. 15, e00655.
-Tao, H. Liu, H. Xie, X. Sun, T. Dong, R. Lu, X. (2022). Preparation and Properties of Nano-ZnO Combined with Biomass Heavy Oil Composite-Modified Asphalt. Adv. Mater. Sci. Eng. 2022, 5179787.
-Vamsikrishna, D. Manikanta, K.V. (2019). Tyre Rubber Modified Bitumen for Ashpalt Mixture. J. Trend Sci. Res. Dev. 3, 42–46.
-Yan, J. Zheng, J. Li, N. (2019). Study on the crack resistance of basalt fiber asphalt mortar. J. Build. Mater. 22, 800–804.
-Zhao, Y. (2014). Experimental study on crack resistance of basalt fiber reinforced asphalt concrete. Highw. Eng. 39, 48–51.
Journal of Transportation Research
Volume 21, Issue 1 - Serial Number 78
February 2024
Pages 355-368

Files

Share

How to cite

Statistics